304 STAINLESS AEROSPACE TUBING
304 STAINLESS AEROSPACE TUBING
304 and 304L are austenitic alloys. These alloys are the most familiar and frequently used alloys in the stainless steel family. The L in 304L refers to a lower carbon content to allow for a greater corrosion protection when welding. Material produced to AMS-T-6845 is suitable for use in high pressure hydraulic systems.
304/304L TUBING TO MIL-T-8504
304 and 304L are austenitic alloys. These alloys are the most familiar and frequently used alloys in the stainless steel family. The L in 304L refers to a lower carbon content to allow for a greater corrosion protection when welding.
304 Stock Size Range:
OD: .250″- 5″
Walls: .006″- .250″
Tempers: 1/8 hard
Specifications: AMS-T-6845, MIL-T-6845, AMS 5566
| Weight % | Ni | Cr | Mn | C | Si | Mo | S | P | Cu |
|---|---|---|---|---|---|---|---|---|---|
| Minimum | 8.00 | 18.00 | |||||||
| Maximum | 10.50 | 20.00 | 2.00 | .08 | 1.00 | .75 | .03 | .045 | .75 |
| Ultimate | Yield | Elongation % |
|---|---|---|
| KSI | PSI | |
| 105-140 | 75-110 min | 20% |
304/304L STOCK SIZE RANGE:
OD: .032″- 5″
Walls: .006″- .250″
Tempers: Annealed
Specifications: MILT 8504, AMS-T-8506, AMS 5560, AMS5567
| Weight % | Ni | Cr | Mn | C | Si | Mo | S | P | Cu |
|---|---|---|---|---|---|---|---|---|---|
| Minimum | 8.00 | 18.00 | |||||||
| Maximum | 12.00 | 20.00 | 2.00 | .08 | 1.00 | .50 | .03 | .045 | .75 |
| Nominal OD | Nominal Wall | Ultimate KSI | Yield KSI | Elongation in 2″ |
|---|---|---|---|---|
| .187 and less | .016 and less | 115 max | 30 | 30 |
| Over .016 | 75-100 | 30 | 40 | |
| Over .187 | .012 and | 110 max | 30 | 37 |
| To .500 incl | Less | |||
| Over .012 | 75-100 | 30 | 40 | |
| Over .500 | All | 75-100 | 30 | 40 |